The inception of our group in 1951 was based on firm principles of quality consciousness, attention to detail combined with cost-effectiveness.
PARTICULARS | HARDNESS HRC | LIFE TIME | |
1. 1.5% Chromium Grade |
58° 60° |
1 TIME 1.25 TIMES |
|
DIN-1.2067 | (SAE-52100) | ||
DIN-1.2419 | (AISI-07) | ||
2. 12% Chromium Grade (skb) | |||
DIN- 1.2379 DIN- 1.2436 |
D2 D6 |
60°± 1 60°± 1 |
2 TIMES 2 TIMES |
3. HSS Quality (skb Supercut) | |||
DIN-1.3343 | M2 | 62°± 1 | 3-4 TIMES |
4. 18% Tungsten Grade (skb Ultra) | |||
DIN-1.3355 | T1 | 63°± 1 | 4-6 TIMES |
5. Powder Metallurgy (Ultra Series 2000) | |||
ASP-2023 | 64°± 1 | 6-8 TIMES | |
6. Powder Metallurgy (skb Futura) | |||
ASP-2053
VANADIS 10 CPM 10V |
64 ± 1 64 ± 1 64 ± 1 |
8-10 Times 8-10 Times 8-10 Times |
|
7. Tungsten Carbide Tipped | Hv30 1750 |
15-20 TIMES |